Supplementary Files
Keywords
Uji Bending
Proses Pengelasan TIG
Kekuatan Bending
How to Cite
Abstract
The purpose of this study was to determine the bending strength of the weld in the connection process with Tungsten Inert Gas (TIG) to the 5083 series aluminum (Al) plate 6 mm thick, the welding was carried out with various current strength treatments, namely 130 A, 140 A, 150 A. and Argon gas discharge of 5 lt/minute, 10 lt/minute, 15 lt/minute in each welding process, and also to find out the defects in the weld area after the bending test was carried out. The method used in this study is the analytical method, which is the method used to test by adding different treatments of current and gas discharge variations during the specimen welding process, so that later on we will get a different welding strength difference in each specimen. From the results obtained from the research on this sample, welding using Argon gas discharge which is
References
Cakra. (2009), “Perubahan Kekuatan Sambungan Las Aluminium Seri 1100 dengan Variasi Kuat Arus Listrik Pada Proses Las Metal Inert Gas (MIG)”, JURNAL ILMIAH TEKNIK MESIN, Vol. 3 No. 1, Hal. 11-17.
Wiryosumarto, H., Dan Okmura, T.,(2000), “Teknologi Pengelasan Logam”, cetakan ke-8, Pradnya Paramita, Jakarta.
Romli. (2012). “Pengaruh Proses Pengelasan TIG Terhadap Sifat Mekanis Bahan Paduan Aluminium”, JURNAL AUSTENIT, Vol. 4, No. 1, Hal. 9-15.
Darsin, M.; Junus, S.; dan Triawan, Y.I.,(2010), “Analisa Sifat Mekanik dan Struktur Mikro Paduan Akuminium 5083 Akibat Pengelasan Metal Inert Gas (MIG) Dengan Variasi Preheat Dan Post Heat”, JURNAL ROTOR, Vol. 3, No. 2, Hal. 67-74.
Tim Penyusun, Fakultas Teknik UNY.,(2004), “Mengelas Dengan Proses Las Gas Tungsten”, Direktorat Jendral Pendidikan Dasar dan Menengah, Departemen Pendidikan Nasional.
Bintoro, A.G.,(2000), “Dasar – Dasar Pekerjaan Las”, Penerbit Kanisius, 55 Yogyakarta.
Anggoro, P.D.; Wilm, A.; dan Hartono, Y.,(2016), “Analisa Kukuatan Mekanik Sambungan Las Metode MIG (Metal Inert Gas) Dan Metode FSW (Friction Stir Welding) 800 RPM Pada Aluminium Tipe 5083”, JURNAL TEKNIK PERKAPALAN, Vol. 4, No. 3, Hal. 613-621.
Widharto, Sri,.(2006). “Petunjuk Kerja Las”, Cetakan Ke-6, Pradnya Paramita, Jakarta.
Widharto, S. 2013. Welding Inspection. Jakarta: Mitra Wacana Media.
Riswadi dan Ilham. 2012. Studi Komparasi Sambungan Lasa Dissimiliar AA5083- AA6061-T6 Antara TIG dan FSW.Industrial Reseach Workshop and National Seminar 2012. ISBN 978-979-3541-25-9. Hlm. 75-79.
Sunaryo, Hery. 2008. Teknik Pengelasan Kapal Jilid 1 untuk Sekolah Menegah Kejuruan. Jakarta : Direktorat Pembinaan Sekolah Menengah Kejuruan
This work is licensed under a Creative Commons Attribution 4.0 International License.