Aluminium 5083
Kuat Arus
Gas Argon
How to Cite
Abstract
In the technology industry, metal raw materials such as steel and aluminum have an important role in the production process, as so far there is no metal that cannot be joined by welding. Metal Inert Gas (MIG) welding method is a gas arc welding that uses a welding wire as well as an electrode. In the Metal Inert Gas (MIG) welding process, the heat from this welding process is generated by a welding arc formed between the wire electrode and the workpiece. The purpose of this study was to determine the tensile strength of the welding results in the connection process with Metal Inert Gas (MIG) against aluminum (Al) 5083 series 6 mm thick, the welding was carried out with various current strength treatments, namely 120 A, 130 A, 140 A. and Argon gas discharge 5 lt/minute, 10 lt/minute, 15 lt/minute in each welding process. This research is useful to know and understand about the analysis of the welding process on aluminum 5083 with a thickness of 6 mm with Metal Inert Gas (MIG) welding process using vertical (3 grove) welding techniques. The method used in this study is the analytical method, which is a method for testing by adding different treatments of current and discharge variations of Argon gas during the welding process of the specimen, so that different welding strengths will be obtained in each specimen.
References
Anggoro, P.D.; Wilm, A.; dan Hartono, Y.,(2016), “Analisa Kukuatan Mekanik Sambungan Las Metode MIG (Metal Inert Gas) Dan Metode FSW (Friction Stir Welding) 800 RPM Pada Aluminium Tipe 5083”, JURNAL TEKNIK PERKAPALAN, Vol. 4, No. 3, Hal. 613-621.
Bintoro, A.G.,(2000), “Dasar – Dasar Pekerjaan Las”, Penerbit Kanisius, 55 Yogyakarta.
Cakra. (2009), “Perubahan Kekuatan Sambungan Las Aluminium Seri 1100 dengan Variasi Kuat Arus Listrik Pada Proses Las Metal Inert Gas (MIG)”, JURNAL ILMIAH TEKNIK MESIN, Vol. 3 No. 1, Hal. 11-17.
Darsin, M.; Junus, S.; dan Triawan, Y.I.,(2010), “Analisa Sifat Mekanik dan Struktur Mikro Paduan Akuminium 5083 Akibat Pengelasan Metal Inert Gas (MIG) Dengan Variasi Preheat Dan Post Heat”, JURNAL ROTOR, Vol. 3, No. 2, Hal. 67-74.
Riswadi dan Ilham. 2012. Studi Komparasi Sambungan Lasa Dissimiliar AA5083- AA6061-T6 Antara TIG dan FSW.Industrial Reseach Workshop and National Seminar 2012. ISBN 978-979-3541-25-9. Hlm. 75-79.
Sunaryo, Hery. 2008. Teknik Pengelasan Kapal Jilid 1 untuk Sekolah Menegah Kejuruan. Jakarta : Direktorat Pembinaan Sekolah Menengah Kejuruan.
Tim Penyusun, Fakultas Teknik UNY.,(2004), “Mengelas Dengan Proses Las Gas Tungsten”, Direktorat Jendral Pendidikan Dasar dan Menengah, Departemen Pendidikan Nasional.
Wiryosumarto, H., Dan Okmura, T.,(2000), “Teknologi Pengelasan Logam”, cetakan ke-8, Pradnya Paramita, Jakarta.
Widharto, Sri,.(2006). “Petunjuk Kerja Las”, Cetakan Ke-6, Pradnya Paramita, Jakarta.
Widharto, S. 2013. Welding Inspection. Jakarta: Mitra Wacana Media.
This work is licensed under a Creative Commons Attribution 4.0 International License.