Keywords
Preheating
Tensile Strength
Welding
SMAW
How to Cite
Abstract
Based on the conducted research, it is concluded that preheating has a significant impact on the tensile strength of welded aluminium 5083. Specifically, preheating at 40°C resulted in the highest ultimate tensile strength of 304.535 MPa, representing an 8.748% increase compared to the non-preheated specimen's 301.894 MPa. Conversely, preheating at 80°C led to a notable decline in tensile strength to 253.521 MPa, a decrease of 16.023%. These findings imply that moderate preheating can enhance the weld quality of aluminium 5083, while excessive preheating adversely affects it. This underscores the importance of optimizing preheating temperatures in welding processes to achieve desired mechanical properties. Further research is recommended to explore the underlying mechanisms affecting tensile strength at various preheating temperatures and to investigate the effects of preheating on other aluminium alloys.
Highlight:
- Preheating at 40°C improves tensile strength by 8.748%.
- Excessive preheating at 80°C decreases tensile strength by 16.023%.
- Optimal preheating temperature crucial for weld quality in aluminium 5083.
Keywoard: Aluminium 5083, Preheating, Tensile Strength, Welding, SMAW
References
I. A. Kuntar, "Studi Eksperimental Friction Stir Welding Aluminium 5083 dengan Variasi Kecepatan Putaran dan Kemiringan Tool," Master's thesis, Institut Teknologi Sepuluh Nopember, Surabaya, 2016.
R. Harsono, S. M. Respati, and H. Purwanto, "Analisis Pengelasan SMAW Tegangan DC terhadap Kekuatan Tarik, Kekerasan, Foto Makro, dan Mikro pada Stainless Steel 304," Jurnal Momentum, vol. XV, pp. 58-63, 2019.
M. Darsin, S. Junusii, and Y. I. Triawan, "Analisa Sifat Mekanik dan Struktur Mikro Paduan Aluminium 5083 Akibat Pengelasan Metal Inert Gas (MIG) dengan Variasi Preheat dan Post Heat," Jurnal ROTOR, vol. 3, no. 2, pp. 67-74, 2010.
B. Bagus, S. M. Respati, and M. Dzulfikar, "Pengaruh Posisi Pengelasan Terhadap Kekuatan Tarik, Foto Makro dan Mikro pada Baja ST 37 dengan Pengelasan SMAW untuk Rangka Billboard," Jurnal Momentum, vol. XV, no. 2, pp. 132-136, 2019.
A. Rifaldi, A. U. Ryadin, and A. R. Hakim, "Pengaruh Suhu Preheating Terhadap Kekuatan Tarik dan Kekerasan Pelat Baja ASTM A36 pada Pengelasan Shielded Metal Arc Welding (SMAW)," Jurnal Sigma Teknika, vol. IV, no. 1, pp. 81-90, 2021.
E. Gunawan, D. Perdana, and M. Subekti, "Analisa Pengaruh Variasi Tipe Sambungan Terhadap Sifat Mekanis pada Pembuatan Tangki BBM dari Bahan Aluminium Dilakukan Dua Welder Secara Bersamaan dengan Menggunakan Pengelasan GTAW," Jurnal Seniati, 2019.
D. Radaj, "Heat Effects of Welding," Berlin: Springer-Verlag, 1992.
R. C. Kusuma, S. Jokosisworo, and A. W. B. Santosa, "Analisis Perbandingan Kekuatan Tarik, Impak, Tekuk dan Mikrografi Aluminium 5083 Pasca Pengelasan TIG (Tungsten Inert Gas) dengan Media Pendingin Air Laut dan Oli," Jurnal Teknik Perkapalan, vol. 5, no. 4, 2017.
Teng and Lin, "Effect of Welding Conditions on Residual Stresses due to Butt Welds," International Journal of Pressure Vessels and Piping, vol. LXXV, pp. 857-864, 1998.
N. Ahmadi, "Pengaruh Suhu Preheat dan Variasi Arus Pada Hasil Las TIG Aluminium Paduan terhadap Kekuatan Tarik dan Kekerasan," Jurnal Angkasa, vol. VIII, no. 1, pp. 159-166, 2016.
Sirama, "Pengaruh Preheat terhadap Laju Perambatan Retak Fatik Sambungan Las TIG pada Pengelasan Aluminium Paduan 6061-T6," 2014.
U. Prasmayobi, "Studi Kekuatan Bending dan Kekerasan pada Pengelasan Aluminium dengan Menggunakan Las SMAW (Shielded Metal Arc Welding)," Skripsi, Jurusan Teknik Mesin, Fakultas Teknik, Universitas Halu Oleo, 2016.
P. Wibowo, "Analisis Pengaruh Preheat atau Pemanasan Awal Terhadap Hasil Pengelasan Ulang Aluminium 5083 Ditinjau dari Sifat Mekanik dan Metalurgi pada Lambung Kapal," Surabaya: Institut Teknologi Sepuluh Nopember, 2015.
S. N. Hidayat, "Pengaruh Suhu Preheat Terhadap Sifat Mekanis (Tarik, Kekerasan) dan Struktur Mikro Sambungan Butt Joint dengan Pengelasan SMAW pada Baja Karbon," Yogyakarta: Institut Teknologi Nasional Yogyakarta, 2016.
D. Y. Akbar, Wartono, and D. R. Hartana, "Pengaruh Temperatur Preheat terhadap Sifat Mekanis Las SMAW pada Baja Karbon," Jurnal Cendekia Mekanika, vol. I, no. 1, pp. 47-56, 2020.
This work is licensed under a Creative Commons Attribution 4.0 International License.